D. M. Kondratiev, K. B. Kalmykov, N. E. Dmitrieva, S. F. Dunaev

The phase equilibria in the Al-Ni-Zr system at 1123 K

Abstract

The phase equlibria in the Al–Ni–Zr system at 1123 K at aluminium concentration up to 45 at.% were investigated by the methods of X-ray and electron probe microanalysis. The fragment of the isothermal crossection of this system is constructed. For the first time there was established the existence of three-phase equilibria: Zr7Ni10 + Zr8Ni21 + Zr2Ni7 , t2 + NiAl + Zr2Ni7, NiAl + Ni3Al + Zr2Ni7, Zr7Ni10 + Zr2Ni7 + t2 at 1123 K. The phase on the basis of the double Zr2Ni7 compound dissolves up to 13 at. % Al. The crystal structure of the phase t7 on the Zr5Ni4Al basis was defined: the structural type is the same as U3Si2, the spatial group is P4/mbm (a = 7,1852 (7) Å, c = 3,3019 (5) Å).
Key words: phase equliribria, X-ray analysis, the electron probe microanalysis, bulk amorphous materials.
Moscow University Chemistry Bulletin.
2012, Vol. 53, No. 6, P. 374
   

Copyright (C) Chemistry Dept., Moscow State University, 2002
   Overview
   Editorial board
   Tables of Contents
   Subscription

The site is supported by Russian Foundation for Basic Research
  The using of published on this page materials is not allowed without special permission
Copyright (C) Chemisty Department of Moscow State University
Web-Editor: B.I.Pokrovskii
Web-design: Copyright (C) MIG and VVM
webmaster@www.chem.msu.su